Multi-gate semiconductor device and method for forming the same

ABSTRACT

Semiconductor structures and method for forming the same are provided. The semiconductor structure includes a substrate and first nanostructures and second nanostructures formed over the substrate. The semiconductor structure further includes a first source/drain structure formed adjacent to the first nanostructures and a second source/drain structure formed adjacent to the second nanostructures. The semiconductor structure further includes a first contact plug formed over the first source/drain structure and a second contact plug formed over the second source/drain structure. In addition, a bottom portion of the first contact plug is lower than a bottom portion of the first nanostructures, and a bottom portion of the second contact plug is higher than a top portion of the second nanostructures.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a Continuation application of U.S. patent application Ser. No. 15/979,123, filed on May 14, 2018, the entire of which is incorporated by reference herein.

BACKGROUND

As the semiconductor industry develops smaller and smaller nanoscale products and processes in pursuit of higher device density, higher performance, and lower costs, the challenges of downscaling both fabrication and design have led to the development of three-dimensional designs, such as multi-gate field effect transistor (FET) including a fin FET (FinFET) and a gate-all-around (GAA) FET. In a FinFET, a gate electrode is positioned adjacent to three side surfaces of a channel region with a gate dielectric layer interposed therebetween. Because the gate structure surrounds the fin on three sides, the transistor essentially has three gates controlling the current through the fin or channel region. However, the fourth side, the bottom part of the channel region, is positioned far away from the gate electrode and thus is not under close gate control. In contrast to a FinFET, a GAA FET includes an arrangement wherein all side surfaces of the channel region are surrounded by the gate electrode, allowing fuller depletion in the channel region and resulting in fewer short-channel effects due to a steeper sub-threshold current swing (SS) and smaller drain induced barrier lower (DIBL).

Although existing GAA FET devices and methods of fabricating GAA FET devices have been generally adequate for their intended purpose, such devices and methods have not been entirely satisfactory in all aspects.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It is noted that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIG. 1 shows a flow chart representing a method for forming a multi-gate semiconductor structure according to aspects of the present disclosure.

FIG. 2 shows a flow chart representing a method for forming a multi-gate semiconductor structure according to aspects of the present disclosure.

FIGS. 3A, 4A, 5A, 6A, 7A, 8A, 9A, 10A, 11A, 12A, 13A, 14A and 15A illustrate a multi-gate semiconductor device at various fabrication stages constructed according to aspects of one or more embodiments of the present disclosure.

FIGS. 3B, 4B, 5B, 6B, 7B, 8B, 9B, 10B, 11B, 12B, 13B, 14B and 15B are cross-sectional views taken along line I-I′ of FIGS. 3A, 4A, 5A, 6A, 7A, 8A, 9A, 10A, 11A, 12A, 13A, 14A and 15A, respectively, according to aspects of one or more embodiments of the present disclosure.

FIGS. 3C, 4C, 5C, 6C, 7C, 8C, 9C, 10C, 11C, 12C, 13C, 14C and 15C are cross-sectional views taken along line II-IP of FIGS. 3A, 4A, 5A, 6A, 7A, 8A, 9A, 10A, 11A, 12A, 13A, 14A and 15A, respectively, according to aspects of one or more embodiments of the present disclosure.

FIGS. 3D, 4D, 5D, 6D, 7D, 8D, 9D, 10D, 11D, 12D, 13D, 14D, and 15D are cross-sectional views taken along line III-III′ of FIGS. 3A, 4A, 5A, 6A, 7A, 8A, 9A, 10A, 11A, 12A, 13A, 14A and 15A, respectively, according to aspects of one or more embodiments of the present disclosure.

FIGS. 4E, 5E, 6E, 7E, 8E, 9E, 10E, 11E, 12E, 13E, 14E, and 15E are cross-sectional views taken along line IV-IV′ of FIGS. 4A, 5A, 6A, 7A, 8A, 9A, 10A, 11A, 12A, 13A, 14A and 15A, respectively, according to aspects of one or more embodiments of the present disclosure.

FIGS. 16A and 17A illustrate a multi-gate semiconductor device at various fabrication stages constructed according to aspects of one or more embodiments of the present disclosure.

FIGS. 16B and 17B are cross-sectional views taken along line I-I′ of FIGS. 16A and 17A, respectively, according to aspects of one or more embodiments of the present disclosure.

FIGS. 16C and 17C are cross-sectional views taken along line II-IP of FIGS. 16A and 17A, respectively, according to aspects of one or more embodiments of the present disclosure.

FIGS. 16D and 17D are cross-sectional views taken along line of FIGS. 16A and 17A, respectively, according to aspects of one or more embodiments of the present disclosure.

FIGS. 16E and 17E are cross-sectional view taken along line IV-IV′ of FIGS. 16A and 17A, respectively, according to aspects of one or more embodiments of the present disclosure.

DETAILED DESCRIPTION

The following disclosure provides many different embodiments, or examples, for implementing different features of the provided subject matter. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper,” “on” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.

As used herein, the terms such as “first,” “second” and “third” describe various elements, components, regions, layers and/or sections, but these elements, components, regions, layers and/or sections should not be limited by these terms. These terms may be only used to distinguish one element, component, region, layer or section from another. The terms such as “first,” “second” and “third” when used herein do not imply a sequence or order unless clearly indicated by the context.

As used herein, the terms “approximately,” “substantially,” “substantial” and “about” are used to describe and account for small variations. When used in conjunction with an event or circumstance, the terms can refer to instances in which the event or circumstance occurs precisely as well as instances in which the event or circumstance occurs to a close approximation. For example, when used in conjunction with a numerical value, the terms can refer to a range of variation of less than or equal to ±10% of that numerical value, such as less than or equal to ±5%, less than or equal to ±4%, less than or equal to ±3%, less than or equal to ±2%, less than or equal to ±1%, less than or equal to ±0.5%, less than or equal to ±0.1%, or less than or equal to ±0.05%. For example, two numerical values can be deemed to be “substantially” the same or equal if a difference between the values is less than or equal to ±10% of an average of the values, such as less than or equal to ±5%, less than or equal to ±4%, less than or equal to ±3%, less than or equal to ±2%, less than or equal to ±1%, less than or equal to ±0.5%, less than or equal to ±0.1%, or less than or equal to ±0.05%. For example, “substantially” parallel can refer to a range of angular variation relative to 0° that is less than or equal to ±10°, such as less than or equal to ±5°, less than or equal to ±4°, less than or equal to ±3°, less than or equal to ±2°, less than or equal to ±1°, less than or equal to ±0.5°, less than or equal to ±0.1°, or less than or equal to ±0.05°. For example, “substantially” perpendicular can refer to a range of angular variation relative to 90° that is less than or equal to ±10°, such as less than or equal to ±5°, less than or equal to ±4°, less than or equal to ±3°, less than or equal to ±2°, less than or equal to ±1°, less than or equal to ±0.5°, less than or equal to ±0.1°, or less than or equal to ±0.05°.

The gate-all-around (GAA) transistor structures may be patterned by any suitable method. For example, the structures may be patterned using one or more photolithography processes, including double-patterning or multi-patterning processes. Generally, double-patterning or multi-patterning processes combine photolithography and self-aligned processes, allowing patterns to be created that have, for example, pitches smaller than what is otherwise obtainable using a single, direct photolithography process. For example, in one embodiment, a sacrificial layer is formed over a substrate and patterned using a photolithography process. Spacers are formed alongside the patterned sacrificial layer using a self-aligned process. The sacrificial layer is then removed, and the remaining spacers may then be used to pattern the GAA structure.

GAA transistor structures may include nanowire structures, which are a promising candidate for logic device applications in future technologies. While downscaling device pitch, external resistance of source/drain and metal contact becomes a dominant factor in determining the device performance, more of a factor than channel resistance. As circuit density and device density increase, metal contact dimensions have to be decreased accordingly in order to minimize the ratio of contact area to the total chip area. Contact resistance is normally inverse to contact area. That is, a smaller contact area will correspond to a greater contact resistance. Further, within a limited contact area, resistance of a metal contact will be increased not only due to a smaller metal volume in the limited contact area, but also due to the inferior current spreading in metal. This makes contact resistance a significant and sometimes dominant factor in very large scale integration (VLSI) metal system performance.

It is therefore concluded that electrical contacts and associated contact resistance, which are required to conduct both power and signals throughout the integrated circuitry, are important in the manufacturing and subsequent operation of integrated circuit devices.

It should be noted that the present disclosure presents embodiments in the form of multi-gate transistors or fin-type multi-gate transistors referred to herein as FinFET devices. The FinFET devices may be GAA devices, Omega-gate (a-gate) devices, Pi-gate (H-gate) devices, dual-gate devices, tri-gate devices, bulk devices, silicon-on-insulator (SOI) devices, and/or other configurations. One of ordinary skill may recognize other examples of semiconductor devices that may benefit from aspects of the present disclosure.

FIG. 1 is a flow chart representing a method for forming a multi-gate semiconductor structure 10 a according to aspects of the present disclosure. The method 10 a includes an operation 102, receiving a substrate including at least a first fin structure and a second fin structure. The method 10 a further includes an operation 104, disposing a dummy gate structure over a portion of the first fin structure and a portion of the second fin structure. The method 10 a further includes an operation 106 a, removing portions of the first fin structure exposed through the dummy gate structure to form at least a first recess in the substrate. The method 10 a further includes an operation 108 a, forming a first semiconductor layer in the first recess. The method 10 a further includes an operation 110, disposing a dielectric structure over the substrate. The method 10 a further includes an operation 112 a, removing a portion of the dummy gate structure to form a first gate trench in the dielectric structure. The method 10 a further includes an operation 114 a, forming a plurality of first nanowires and a first gate structure in the first gate trench. The method 10 a further includes an operation 116 a, removing a portion of the dielectric structure to form a first opening in the dielectric structure. The method 10 a further includes an operation 118 a, forming a first metal silicide layer over the first semiconductor layer in the first opening. The method 10 a further includes an operation 120 a, disposing a metal layer to fill the first opening. The method 10 a will be further described according to one or more embodiments. It should be noted that the operations of the method for forming the multi-gate semiconductor device 10 a may be rearranged or otherwise modified within the scope of the various aspects. It should be further noted that additional processes may be provided before, during, and after the method 10 a, and that some other processes may be only briefly described herein. Thus other implementations are possible within the scope of the various aspects described herein.

FIG. 2 is a flow chart representing a method for forming a multi-gate semiconductor structure 10 b according to aspects of the present disclosure. In some embodiments, the method 10 b and the method 10 a share similar operations, but the disclosure is not limited thereto. The method 10 b includes the operation 102, receiving a substrate including at least a first fin structure and a second fin structure. The method 10 b further includes the operation 104, disposing a dummy gate structure over a portion of the first fin structure and a portion of the second fin structure. The method 10 b further includes an operation 106 b, removing portions of the second fin structure exposed through the dummy gate structure to form at least a second recess in the substrate and a plurality of nanowires suspended in the second recess. The method 10 b further includes an operation 108 b, forming a second semiconductor layer surrounding each of the plurality of second nanowires. The method 10 b further includes the operation 110, disposing a dielectric structure over the substrate. The method 10 b further includes an operation 112 b, removing a portion of the dummy gate structure to form a second gate trench in the dielectric structure. The method 10 b further includes an operation 114 b, forming a plurality of third nanowires and a second gate structure in the second gate trench. The method 10 b further includes an operation 116 b, removing a portion of the dielectric structure to form a second opening in the dielectric structure. The method 10 b further includes an operation 118 b, forming a second metal silicide layer over the second semiconductor layer. The method 10 b further includes an operation 120 b, disposing a metal layer to fill the second opening. The method 10 b will be further described according to one or more embodiments. It should be noted that the operations of the method for forming the multi-gate semiconductor device 10 b may be rearranged or otherwise modified within the scope of the various aspects. Further, the method 10 a and the method 10 b can be integrated, and thus similar operations can be performed simultaneously. In some embodiments, operations 116 b and 118 b of the method 10 b are performed after operations 116 a and 118 a of the method 10 a. In other embodiments, operations 116 a and 118 a of the method 10 a and operations 116 b and 118 b of the method 10 b are simultaneously performed. It should be further noted that additional processes may be provided before, during, and after the method 10 b, and that some other processes may be only briefly described herein. Thus other implementations are possible within the scope of the various aspects described herein.

FIGS. 3A, 4A, 5A, 6A, 7A, 8A, 9A, 10A, 11A, 12A, 13A, 14A, and 15A are drawings illustrating a multi-gate semiconductor device 300 at various fabrication stages constructed according to aspects of one or more embodiments the present disclosure. FIGS. 3B, 4B, 5B, 6B, 7B, 8B, 9B, 10B, 11B, 12B, 13B, 14B, and 15B are cross-sectional views taken along line I-I′ of FIGS. 3A, 4A, 5A, 6A, 7A, 8A, 9A, 10A, 11A, 12A, 13A, 14A, and 15A, respectively, according to aspects of one or more embodiments of the present disclosure, FIGS. 3C, 4C, 5C, 6C, 7C, 8C, 9C, 10C, 11C, 12C, 13C, 14C, and 15C are cross-sectional views taken along line II-IP of FIGS. 3A, 4A, 5A, 6A, 7A, 8A, 9A, 10A, 11A, 12A, 13A, 14A, and 15A, respectively, according to aspects of one or more embodiments of the present disclosure, FIGS. 3D, 4D, 5D, 6D, 7D, 8D, 9D, 10D, 11D, 12D, 13D, 14D, and 15D are cross-sectional views taken along line III-III′ of FIGS. 3A, 4A, 5A, 6A, 7A, 8A, 9A, 10A, 11A, 12A, 13A, 14A, and 15A, respectively, according to aspects of one or more embodiments of the present disclosure, and FIGS. 4E, 5E, 6E, 7E, 8E, 9E, 10E, 11E, 12E, 13E, 14E, and 15E are cross-sectional views taken along line IV-IV′ of FIGS. 4A, 5A, 6A, 7A, 8A, 9A, 10A, 11A, 12A, 13A, 14A, and 15A, respectively, according to aspects of one or more embodiments of the present disclosure. As shown in FIGS. 3A to 3D, a substrate 202 is provided. In some embodiments, the substrate 202 may be a semiconductor substrate such as a silicon substrate. The substrate 202 may also include other semiconductors such as germanium (Ge), silicon carbide (SiC), silicon germanium (SiGe), or diamond. Alternatively, the substrate 202 may include a compound semiconductor and/or an alloy semiconductor. The substrate 202 may include various layers, including conductive or insulating layers formed on a semiconductor substrate. The substrate 202 may include various doping configurations depending on design requirements as is known in the art. For example, different doping profiles (e.g., n wells, p wells) may be formed on the substrate 202 in regions 202 a and 202 b designed for different device types (e.g., n-type field effect transistors (NFET), or p-type field effect transistors (PFET)), as shown in FIGS. 3C and 3D. The suitable doping may include ion implantation of dopants and/or diffusion processes. The substrate 202 typically has isolation features (e.g., shallow trench isolation (STI) features) 204 interposing the regions 202 a and 202 b providing different device types. Further, the substrate 202 may optionally include an epitaxial layer (epi-layer), may be strained for performance enhancement, may include an SOI structure, and/or may have other suitable enhancement features. A stack including semiconductor layers is formed over the substrate 202. In some embodiments, a strain relaxed buffer (SRB) layer (not shown) can be formed over the substrate 202. The SRB layer may be different in composition from the substrate 202 in order to create lattice strain at the interface with the substrate 202. For example, in some embodiments, the substrate 202 includes silicon and is substantially free of germanium while the SRB layer includes SiGe.

Still referring to FIGS. 3A to 3D, a stack including semiconductor layers is formed over the substrate 202. In embodiments that include an SRB layer disposed on the substrate 202, the stack of semiconductor layers may be disposed on the SRB layer. The stack of semiconductor layers may include alternating layers of different compositions. For example, in some embodiments, the stack includes semiconductor layers 206 of a first composition alternating with semiconductor layers 208 of a second composition. By way of example, growth of the layers of the stack may be performed by a molecular beam epitaxy (MBE) process, a metalorganic chemical vapor deposition (MOCVD) process, and/or other suitable epitaxial growth processes. Although five semiconductor layers 206 and five semiconductor layers 208 are shown, it should be understood that the stack may include any number of layers of any suitable composition with various examples including between 2 and 10 semiconductor layers 206 and between 2 and 10 semiconductor layers 208. As explained below, the different compositions of the layers in the stack (e.g., semiconductor layers 206 and semiconductor layers 208) may be used to selectively process some of the layers. Accordingly, the compositions may have different oxidation rates, etchant sensitivity, and/or other differing properties. The semiconductor layers 206 and 208 may have thicknesses chosen based on device performance considerations. In some embodiments, the semiconductor layers 206 are substantially uniform in thickness, and the semiconductor layers 208 are substantially uniform in thickness. In some embodiments, the thickness of the semiconductor layers 206 can be less than the thickness of the semiconductor layers 208, but the disclosure is not limited thereto. For example but not limited thereto, the thickness of the semiconductor layers 206 can be approximately 6 nanometers (nm), and the thickness of the semiconductor layers 208 can be approximately 8 nm.

In some embodiments, the semiconductor layers 208 may include a first semiconductor material such as Si while the semiconductor layers 206 may include the first semiconductor material and a second semiconductor material with a lattice constant greater than a lattice constant of the first semiconductor material. For example, the semiconductor layers 206 may include SiGe, but the disclosure is not limited thereto. Additionally, Ge concentration in the semiconductor layers 206 can be less than or equal to approximately 50%, but the disclosure is not limited thereto. In other embodiments, the semiconductor layers 206 may include other materials such as a compound semiconductor such as SiC, gallium arsenide (GaAs), gallium phosphide (GaP), indium phosphide (InP), indium arsenide (InAs), and/or indium antimonide (InSb), an alloy semiconductor such as SiGe, GaAsP, AlInAs, AlGaAs, InGaAs, GaInP, and/or GaInAsP, or combinations thereof. In some embodiments, the semiconductor layers 206 and 208 may be undoped or substantially dopant-free, where, for example, no doping is performed during the epitaxial growth process. Alternatively, the semiconductor layers 206 and 208 may be doped. For example, the semiconductor layers 206 or 208 may be doped with a p-type dopant such as boron (B), aluminum (Al), In, and Ga for forming a p-type channel, or an n-type dopant such as P, As, Sb, for forming an n-type channel.

Still referring to FIGS. 3A to 3D, at least a first fin structure 210 a and at least a second fin structure 210 b are formed over the substrate 202 from the stack of semiconductor layers 206/208. The first fin structure 210 a and the second fin structure 210 b may be fabricated using suitable operations including photolithography and etch operations. In some embodiments, forming the first and second fin structures 210 a and 210 b may further include a trim process to decrease the width and/or the height of the first and second fin structures 210 a and 210 b. The trim process may include wet or dry etching processes. The height and width of the first and second fin structures 210 a and 210 b may be chosen based on device performance considerations. Further, the first and second fin structures 210 a and 210 b can extend along a first direction D1 as shown in FIGS. 3A to 3D. Accordingly, the substrate 202 including the at least one first fin structure 210 a and at least one second fin structure 210 b is received according to operation 102 of the method 10 a and the method 10 b.

Referring to FIGS. 4A to 4E, in some embodiments, a liner 209 can be formed over the first fin structure 210 a, the second fin structure 210 b and the substrate 202. Next, a dummy gate structure 212 is disposed over a portion of the first fin structure 210 a and a portion of the second fin structure 210 b according to operation 104 of the method 10 a and the method 10 b. The dummy gate structure 212 may be replaced at a later processing stage by a high-K dielectric layer (HK) and metal gate electrode (MG) as discussed below. In some embodiments, the dummy gate structure 212 is formed over the substrate 202 and extends along a second direction D2, which is not parallel with the first direction D1. Additionally, the first direction D1 and the second direction D2 are in the same plane. As shown in FIGS. 4A to 4D, the portion of the first fin structure 210 a underlying the dummy gate structure 212 may be referred to as the channel region, and the portion of the second fin structure 210 b underlying the dummy gate structure 212 may be referred to as the channel region. The dummy gate structure 212 may also define a source/drain region of the first fin structure 210 a, for example, portions of the first fin structure 210 a adjacent to and on opposing sides of the channel region. Similarly, the dummy gate structure 212 may also define a source/drain region of the second fin structure 210 b, for example, portions of the second fin structure 210 b adjacent to and on opposing sides of the channel region. In some embodiments, the dummy gate structure 212 can include at least a polysilicon layer and a patterned hard mask for defining the dummy gate structure.

Still referring to FIGS. 4A to 4E, a spacer 214 can be disposed over sidewalls of the dummy gate structure 212, and portions of the first and second fin structures 210 a and 210 b are exposed through the dummy gate structure 212 and the spacer 214. In some embodiments, the spacer 214 includes insulating materials. As shown in FIGS. 4A, 4C and 4D, the sidewalls of the dummy gate structure 212 are covered by the spacer 214. In some embodiments, portions of the liner 209 can be removed during or after the forming of the spacer 214, and thus portions of the first and second fin structures 210 a and 210 b are exposed as shown in FIGS. 4C to 4E.

Referring to FIGS. 5A to 5E, next, the portions of the first fin structure 210 a exposed through the dummy gate structure 212 and the spacer 214 are removed according to operation 106 a. In some embodiments, portions of the semiconductor layers 206 and portions of the semiconductor layers 208 exposed through the dummy gate structure 212 and the spacer 214 are removed, thereby forming at least a first recess 216 a in the substrate 202 as shown in FIG. 5C. In some embodiments, a patterned protecting layer (not shown) is formed over the second fin structure 210 b or deposited over the region 202 b. Thus the second fin structure 210 b is protected and impervious to the formation of the first recess 216 a. The semiconductor layers 206, and the semiconductor layers 208 are exposed through sidewalls of the first recess 216 a and the substrate 202 is exposed through a bottom of the first recess 216 a. In some embodiments, a portion of each of the exposed semiconductor layers 206 is removed and thus a plurality of notches (not shown) are formed. In some embodiments, an insulating layer (not shown) is formed over the substrate 202 and a suitable etching operation is then performed. Thus, a plurality of inner spacers 211 a are formed in the notches as shown in FIG. 5C. Consequently, the semiconductor layers 208 and the inner spacers 211 a are exposed. In other words, the semiconductor layers 206 are enclosed by the semiconductor layers 208 and the inner spacers 211 a. In some embodiments, the inner spacers 211 a include one or more insulating materials such as SiN, SiO, SiC, SiOC, SiOCN, other materials, or a combination thereof, but the disclosure is not limited thereto.

Still referring to FIGS. 5A to 5E, a first semiconductor layer 220 a is formed in the first recess 216 a according to operation 108 a of the method 10 a. In some embodiments, the first semiconductor layer 220 a is a doped epitaxial semiconductor layer. In some embodiments, the first semiconductor layer 220 a is a phosphorus-doped silicon (SiP) epitaxial layer, but the disclosure is not limited thereto. Additionally, the first semiconductor layer 220 a covers the semiconductor layers 208, the inner spacers 211 a and the bottom of the first recess 216 a. Subsequently, the patterned protecting layer is removed from the substrate 202 after the forming of the first semiconductor layer 220 a as shown in FIGS. 5A to 5E. In some embodiments, a thickness of the first semiconductor layer 220 a is between approximately 10 nm and approximately 20 nm, but the disclosure is not limited thereto.

Referring to FIGS. 6A to 6E, next, portions of the second fin structure 210 b exposed through the dummy gate structure 212 and the spacer 214 are removed according to operation 106 b of the method 10 b. In some embodiments, portions of the semiconductor layers 208 are removed, thereby forming at least a second recess 216 b in the substrate 202 according to operation 106 b. Significantly, a plurality of nanowires 230, which previously comprised the semiconductor layers 206, are formed in the second recess 216 b according to operation 106 b, as shown in FIGS. 6D and 6E. In some embodiments, a patterned protecting layer (not shown) is formed to fill the first recess 216 a or deposited over the region 202 a, and thus the first semiconductor layer 220 a is protected and impervious to the formation of the second recess 216 b and the plurality of nanowires 230. As shown in FIGS. 6D and 6E, the plurality of nanowires 230 are suspended in and exposed through the second recess 216 b, the semiconductor layers 208 are exposed through sidewalls of the second recess 216 b, and the substrate 202 is exposed through a bottom of the second recess 216 b.

Referring to FIGS. 7A to 7E, a portion of the exposed semiconductor layers 208 is then removed and thus a plurality of notches (not shown) are formed. In some embodiments, an insulating layer (not shown) is formed over the substrate 202 and a suitable etching operation is subsequently performed. Thus, a plurality of inner spacers 211 b are formed in the notches and over the substrate 202, as shown in FIG. 7D. In other words, the semiconductor layers 208 are enclosed by the semiconductor layers 206 and the inner spacers 211 b. In some embodiments, the inner spacers 211 b include one or more insulating materials such as SiN, SiO, SiC, SiOC, SiOCN, other materials, or a combination thereof, but the disclosure is not limited thereto.

Still referring to FIGS. 7A to 7E, a second semiconductor layer 220 b is formed in the second recess 216 b according to operation 108 b of the method 10 b. The second semiconductor layer 220 b is formed to surround each of the nanowires 230, as shown in FIG. 7E. In some embodiments, the second semiconductor layer 220 b includes the first semiconductor material and the second semiconductor material. For example but not limited thereto, the second semiconductor layer 220 b can include SiGe, and a Ge concentration of the second semiconductor layer 220 b is greater than the Ge concentration of the plurality of nanowires 230, which previously comprised the semiconductor layers 206. In some embodiments, the Ge concentration of the second semiconductor layer 220 b is greater than 50%, but the disclosure is not limited thereto. In some embodiments, the Ge concentration of the second semiconductor layer 220 b is between approximately 50% and approximately 70%, but the disclosure is not limited thereto. In some embodiments, the second semiconductor layer 220 b is a doped epitaxial semiconductor layer. For example but not limited thereto, the second semiconductor layer 220 b can be a boron-doped silicon germanium (SiGeB) epitaxial layer. Further, the patterned protecting layer is removed from the substrate 202 after the forming of the second semiconductor layer 220 b. In some embodiments, the method 10 a and the method 10 b are integrated such that operations 106 b and 108 b of the method 10 b are performed after operations 106 a and 108 a of the method 10 a. However, operations 106 b and 108 b of the method 10 b can performed before operations 106 a and 108 a of the method 10 a in other embodiments.

Referring to FIGS. 8A to 8E, a dielectric structure 240 is disposed over the substrate 202 according to operation 110 of the method 10 a and the method 10 b. The dielectric structure 240 fills the first recess 216 a and the second recess 216 b. In some embodiments, the dielectric structure 240 can include an etch-stop layer (e.g., a contact etch stop layer (CESL)) 242 and various dielectric layers (e.g., an inter-layer dielectric (ILD) layer) 244 formed on the substrate 202 after the forming of the second semiconductor layer 220 b. In some embodiments, the CESL 242 includes a SiN layer, a SiCN layer, a SiON layer, and/or other materials known in the art. In some embodiments, the ILD layer 244 includes materials such as tetraethylorthosilicate (TEOS) oxide, un-doped silicate glass, or doped silicon oxide such as borophosphosilicate glass (BPSG), fused silica glass (FSG), phosphosilicate glass (PSG), boron doped silicon glass (BSG), and/or other suitable dielectric materials. In some embodiments, after the CESL 242 and the ILD layer 244 are deposited, a planarization process, such as a chemical mechanical planarization (CMP) operation, may be performed to form the dielectric structure 240 and to expose a top surface of the dummy gate structure 212 as shown in FIGS. 8A to 8D. In some embodiments, the planarization is performed to expose at least a top surface of the polysilicon layer of the dummy gate structure 212.

Referring to FIGS. 9A to 9E, a portion of the dummy gate structure 212 is subsequently removed to form a first gate trench 218 a in the dielectric structure 240 according to operation 112 a. In some embodiments, a patterned protecting layer (not shown) is formed over the region 202 b, and thus elements in the region 202 b are protected and impervious to the formation of the first gate trench 218 a. As shown in FIG. 9C, the spacer 214 is exposed through sidewalls of the first gate trench 218 a, and the first fin structure 210 a is exposed through the first gate trench 218 a. Subsequently, the liner layer 209 disposed over the first fin structure 209 is removed, and the semiconductor layers 206 are then removed. Accordingly, a plurality of nanowires 232, which previously comprised the semiconductor layers 208, are formed in the first gate trench 218 a according to operation 114 a of the method 10 a, as shown in FIGS. 9B and 9C. Further, the plurality of nanowires 232 serving as channel regions are suspended in the first gate trench 218 a. In some embodiments, the nanowires 232 can be slightly etched to obtain various desirable dimensions and shapes, and the various desired dimensions and shapes may be chosen based on device performance considerations. As shown in FIG. 9C, the plurality of nanowires 232 and the inner spacers 211 a are therefore exposed through the first gate trench 218 a. The patterned protecting layer is then removed.

Referring to FIGS. 10A to 10E, another portion of the dummy gate structure 212 is then removed to form a second gate trench 218 b in the dielectric structure 240 according to operation 112 b of the method 10 b. In some embodiments, another patterned protecting layer (not shown) is formed over the region 202 a, and thus elements in the region 202 a are protected and impervious to the formation of the second gate trench 218 b. As shown in FIG. 10C, the spacer 214 is exposed through sidewalls of the second gate trench 218 b, and the second fin structure 210 b is exposed through the second gate trench 218 b. Subsequently, the liner layer 209 disposed over the second fin structure 210 b is removed, and the semiconductor layers 208 are removed. Accordingly, a plurality of nanowires 234, which previously comprised the semiconductor layers 206, are formed in the second gate trench 218 b according to operation 114 b of the method 10 b, as shown in FIGS. 10B and 10D. Further, the plurality of nanowires 234 serving as channel regions are suspended in the second gate trench 218 b. In some embodiments, the nanowires 234 can be slightly etched to obtain various desirable dimensions and shapes, and the various desired dimensions and shapes may be chosen based on device performance considerations. As shown in FIG. 10D, the plurality of nanowires 234 and the inner spacers 211 b are therefore exposed through the second gate trench 218 b. The patterned protecting layer is then removed. Additionally, the plurality of nanowires 230 and the plurality of nanowires 234, both of which previously comprised the semiconductor layers 206, include the same materials. Further, each of the nanowires 234 is coupled to each of the nanowires 230, as shown in FIG. 10D. In other words, each of the nanowires 234 is coupled to a corresponding nanowire 230. In some embodiments, it is referred that the nanowires 230 and nanowires 234 are the same nanowires, as shown in FIG. 10.

Referring to FIGS. 11A to 11E, an interfacial layer (IL) 252 is formed to surround each of the nanowires 232 exposed in the first gate trench 218 a and each of the nanowires 234 exposed in the second gate trench 218 b, as shown in FIG. 11B. In some embodiments, the IL 252 may include an oxide-containing material such as SiO or SiON. After the forming of the IL 252, a gate dielectric layer 254 is formed over the IL 252. As shown in FIG. 11B, the gate dielectric layer 254 surrounds each of the nanowires 232 and each of the nanowires 234. In some embodiments, the gate dielectric layer 254 includes a high-k dielectric material having a high dielectric constant, for example, a dielectric constant greater than that of thermal silicon oxide ({tilde over ( )}3.9). The high-k dielectric material may include hafnium oxide (HfO₂), zirconium oxide (ZrO₂), lanthanum oxide (La₂O₃), aluminum oxide (Al₂O₃), titanium oxide (TiO₂), yttrium oxide (Y₂O₃), strontium titanate (SrTiO₃), hafnium oxynitride (HfO_(x)N_(y)), other suitable metal-oxides, or combinations thereof.

Still referring to FIGS. 11A to 11E, after the forming of the gate dielectric layer 254, a first gate conductive layer 256 a is disposed in the first gate trench 218 a according to operation 114 a of the method 10 a, and a second gate conductive layer 256 b is disposed in the second gate trench 218 b according to operation 114 b of the method 10 b. The first and second gate conductive layers 256 a and 256 b are formed on the gate dielectric layer 254. In some embodiments, the first gate conductive layer 256 a is formed for an n-channel FET, and the second gate conductive layer 256 b is formed for a p-channel FET. In some embodiments, the first gate conductive layer 256 a can include at least a barrier metal layer (not shown) and a first work function layer, and the second gate conductive layer 256 b can include at least a barrier metal layer (not shown) and a second work function metal layer. The barrier metal layer can include, for example but not limited to, TiN. The first work function metal layer, which provides proper work function to the n-channel FET, includes one or more of TaN, TaAlC, TiN, TiC, Co, TiAl, HfTi, TiSi and TaSi, but the disclosure is not limited thereto. The second work function metal layer, which provides proper work function to the p-channel FET, includes one or more of TiAlC, Al, TiAl, TaN, TaAlC, TiN, TiC and Co, but the disclosure is not limited thereto. Next, a gap-filling metal layer 258 is formed to fill the first gate trench 218 a and the second gate trench 218 b. The gap-filling metal layer 258 can include conductive material, such as Al, Cu, AlCu, or W, but is not limited to the above-mentioned materials. Accordingly, a first gate structure 250 a is formed in the first gate trench 218 a, and a second gate structure 250 b is formed in the second gate trench 218 b, as shown in FIGS. 11A to 11E.

Referring to FIGS. 12A to 12E, a patterned protecting layer 260 is then formed over the dielectric structure 240 and the first and second gate structures 250 a and 250 b. The patterned protecting layer 260 serves as an etching mask for the subsequent operations. Next, a portion of the dielectric layer 240 is removed through the patterned protecting layer 260, and thus at least a first opening 262 a is formed in the dielectric structure 240 according to operation 116 a of the method 10 a. Further, the first semiconductor layer 220 a is exposed in a lower portion of the first opening 262 a while the dielectric structure 240 and the spacers 214 are exposed in an upper portion of the first opening 262 a, as shown in FIGS. 12C and 12E.

Referring to FIGS. 13A to 13E, a first metal silicide layer 270 a is then formed over the first semiconductor layer 220 a according to operation 118 a of the method 10 a. The first metal silicide layer 270 a includes the first semiconductor material and a first metal material. In some embodiments, the first metal silicide layer 270 a can be formed by depositing a metallic layer such as a TiN layer over the first semiconductor layer 220 a. Next, a thermal operation is performed. Consequently, a portion of the first semiconductor layer 220 a reacts with the metallic layer, and the first metal silicide layer 270 a is formed. Therefore, the first metal silicide layer 270 a can include TiSi_(x), but the disclosure is not limited thereto. A thickness of the first semiconductor layer 220 a is reduced to between approximately 5 nm and approximately 15 nm, but the disclosure is not limited thereto. Additionally, since the first metal silicide layer 270 a is formed only over the first semiconductor layer 220 a, the first metal silicide layer 270 a is exposed in the lower portion of the first opening 262 a, as shown in FIG. 13C. In some embodiments, a glue layer 272 including TiN can be formed over the first metal silicide layer 270 a and sidewalls of the upper portion of the first opening 262 a. However, in other embodiments, the glue layer 272 can be omitted.

Referring to FIGS. 14A to 14E, a portion of the dielectric layer 240 is further removed to form at least a second opening 262 b in the dielectric structure 240 according to operation 116 b of the method 10 b. Further, the second semiconductor layer 220 b is exposed in a lower portion of the second opening 262 b while the dielectric structure 240 and the spacers 214 are exposed in an upper portion of the second opening 262 b, as shown in FIGS. 14D and 14E.

Referring to FIGS. 15A to 15E, a second metal silicide layer 270 b is then formed over the second semiconductor layer 220 b according to operation 118 b of the method 10 b. The second metal silicide layer 270 b includes the first semiconductor material, the second semiconductor material, and a second metal material. In some embodiments, the second metal material of the second metal silicide layer 270 b is different from the first metal material of the first metal silicide layer 270 a. In some embodiments, the first metal silicide layer 270 a includes TiSi_(x), and the second metal silicide layer 270 b includes NiSiGe_(x), but the disclosure is not limited thereto. In some embodiment, a Ni layer is formed over the second semiconductor layer 220 b, which is exposed in the lower portion of the second opening 262 b, by suitable operation, such as chemical vapor deposition (CVD). Subsequently, anneal is performed such that Ni and SiGe are reacted and thus NiSiGe_(X) silicide layer 270 b is formed. The superfluous Ni layer is then removed. Additionally, since the second metal silicide layer 270 b is formed only over the second semiconductor layer 220 b, the second metal silicide layer 270 b is exposed in the lower portion of the second opening 262 b, as shown in FIG. 15E. In some embodiments, a glue layer 272 including TiN can be formed over the second metal silicide layer 270 b and sidewalls of the upper portion of the second opening 262 b. However, in other embodiments, the glue layer 272 can be omitted. Additionally, because thermal budget of Ni is lower than that of Ti, the first metal silicide layer 270 a is formed before forming the second opening 262 b and the second metal silicide layer 270 b, but the disclosure is not limited thereto.

Still referring to FIGS. 15A to 15E, a metal layer 264 is next disposed to fill the first opening 262 a and the second opening 262 b according to operation 120 a of the method 10 a and operation 120 b of the method 10 b. In some embodiments, the metal layer 264 includes low-resistivity metal material, such as tungsten (W), but the disclosure is not limited thereto. Accordingly, at least a first conductor, such as a first metal portion 280 a, is formed in the first opening 262 a and a second conductor, such as a second metal portion 280 b, is formed in the second opening 262 b. As shown in FIGS. 15C and 15D, a bottom and sidewalls of a lower portion of the first metal portion 280 a in the first opening 262 a are surrounded by the first silicide layer 270 a while sidewalls of an upper portion of the first metal portion 280 a in the first openings 262 a are surrounded by the spacer 214 and patterned protecting layer 260. Further, the bottom of the second metal portion 280 b in the first opening 262 a is lower than the plurality of nanowires 232, as shown in FIG. 15C. In contrast to the first metal portion 280 a, a lower portion of the second metal portion 280 b in the second openings 262 b surrounds the second metal silicide layer 270 b, as shown in FIGS. 15D and 15E.

Accordingly, a multi-gate semiconductor device 200 a is obtained. As shown in FIG. 15C, the multi-gate semiconductor device 200 a includes the plurality of nanowires 232, the first gate structure 250 a over the plurality of nanowires 232, and source/drain structures 282 a and 284 a at two ends of each nanowire 232. The source/drain structures 282 a and 284 a include the first semiconductor layer 220 a, the first metal portion 280 a, and the first metal silicide layer 270 a sandwiched between the first semiconductor layer 220 a and the lower portion of the first metal portion 280 a. Notably, a bottom surface of the first metal portion 280 a is lower than the plurality of nanowires 232, as shown in FIG. 15C. Further, each of the first semiconductor layer 220 a and the first metal silicide layer 270 a substantially includes a U shape. Additionally, the first gate structure 250 a can include a metal gate structure, but the disclosure is not limited thereto.

According to the multi-gate semiconductor device 200 a, after the forming of the first semiconductor layer 220 a and the first metal silicide layer 270 a, there is still a space for forming the metal layer 264 in the first opening 262 a, and thus the first metal portion 280 a is obtained. Accordingly, the lower region of the first metal portion 280 a can serve as a portion of the source/drain structures 282 a and 284 a while an upper region of the first metal portion 280 a can serve as a contact plug for providing electrical connection between the source/drain structures 282 a and 284 a and other devices or circuits. More importantly, the first metal portion 280 a can include low-resistivity metal material such as the aforementioned W, thereby reducing contact resistance.

In another embodiment, a multi-gate semiconductor device 200 is provided. The multi-gate semiconductor device 200 includes the multi-gate semiconductor structure 200 a and a multi-gate semiconductor structure 200 b. In some embodiments, the multi-gate semiconductor device 200 is a CMOS device, and the multi-gate semiconductor structure 200 a is an n-channel FET and the multi-gate semiconductor structure 200 b is a p-channel FET. As shown in FIGS. 15A to 15E, the multi-gate semiconductor device 200 includes the plurality of nanowires 232 serving as channel regions for the n-channel multi-gate semiconductor structure 200 a and the plurality of nanowires 234 serving as channel regions for the p-channel multi-gate semiconductor structure 200 b. The multi-gate semiconductor device 200 further includes the first gate structure 250 a disposed over the plurality of nanowires 232, the second gate structure 250 b disposed over the plurality of nanowires 234, the first source/drain structures 282 a and 284 a disposed at two ends of each nanowire 232, and second source/drain structures 282 b and 284 b disposed at two ends of each nanowire 234. It should be noted that the first source/drain structures 282 a and 284 a include a conductor such as the first metal portion 280 a, the first semiconductor layer 220 a disposed around sidewalls and a bottom of the lower portion of the first metal portion 280 a, and the first metal silicide layer 270 a disposed between the lower portion of the first metal portion 280 a and the first semiconductor layer 220 a. The second source/drain structures 282 b and 284 b include the plurality of nanowires 230, the second metal silicide layer 270 b disposed over the plurality of nanowires 230, and the second semiconductor layer 220 b disposed between the second metal silicide layer 270 b and the plurality of nanowires 230. Further, the nanowires 230 and the nanowires 234 are the same nanowires. It is referred that a portion of each nanowire surrounded by the second gate structure 250 b serve as channel regions and are referred to as a first portion 234, while another portion of each nanowire adjacent to and on opposing sides of the channel region form a part of the second sour/drain structures 282 b and 284 b and are referred to as a second portion 230.

As mentioned above, the first metal silicide layer 270 a and the second metal silicide layer 270 b can include different semiconductor materials and different metal materials. In some embodiments, the first metal silicide layer 270 a includes TiSi while the second metal silicide layer 270 b includes NiSiGe. It should be noted that for the n-channel multi-gate semiconductor structure 200 a, the contact resistance is reduced by forming the low-resistivity first metal portion 280 a having the bottom surface lower than the plurality of nanowires 232. For the p-channel multi-gate semiconductor structure 200 b, the contact resistance is reduced by forming the Ni-silicide layer, because Ni resistance is lower than Ti resistance. Accordingly, the contact resistance of the multi-gate semiconductor device 200 is reduced by the dual contact formation.

FIGS. 16A and 17A illustrate a multi-gate semiconductor device 200′ at various fabrication stages constructed according to aspects of one or more embodiments of the present disclosure. FIG. 16B and FIG. 17B are cross-sectional views taken along line I-I′ of FIGS. 16A and 17A, respectively, according to aspects of one or more embodiments of the present disclosure, FIGS. 16C and 17C are cross-sectional views taken along line II-IP of FIGS. 16A and 17A, respectively, according to aspects of one or more embodiments of the present disclosure, FIGS. 16D and 17D are cross-sectional views taken along line of FIGS. 16A and 17A, respectively, according to aspects of one or more embodiments of the present disclosure, and FIGS. 16E and 17E are cross-sectional views taken along line IV-IV′ of FIGS. 16A and 17A, respectively, according to aspects of one or more embodiments of the present disclosure. It should be noted that similar elements in FIGS. 3A to 15E and FIGS. 16A to 17E are designated by the same numerals. Further, similar elements in FIGS. 3A to 15E and FIGS. 16A to 17E can include similar materials and can be formed by similar steps; therefore such redundant details are omitted in the interest of brevity.

Please refer to FIGS. 16A to 16E. In some embodiments, operations 102, 104, 106 a and 108 a, 106 b and 108 b, 110, 112 a and 114 a, and 112 b and 114 b are performed, and operations 116 a and 116 b are simultaneously performed after the forming of the first and second gate structures 250 a and 250 b. Consequently, a first opening 262 a and a second opening 262 b are simultaneously formed in the dielectric layer 240. As shown in FIGS. 16A to 16E, the first semiconductor layer 220 a is exposed in the first opening 262 a and the second semiconductor layer 220 b is exposed in the second opening 262 b. In some embodiments, the first semiconductor layer 220 a forms a bottom and sidewalls of a lower portion of the first opening 262 a while the second semiconductor layer 220 b protrudes from a bottom of the second opening 262 b, as shown in FIGS. 16C and 16E.

Referring to FIGS. 17A to 17E, a first metal silicide layer 270 a′ is formed over the first semiconductor layer 220 a and a second metal silicide layer 270 b′ is formed over the second semiconductor layer 220 b according to operations 118 a and 118 b. Notably, the operations 118 a and 118 b are performed at the same time, and thus the first metal silicide layer 270 a′ and the second metal silicide layer 270 b′ are simultaneously formed. The first metal silicide layer 270 a′ includes the first semiconductor material and a first metal material, and the second metal silicide layer 270 b′ includes the first semiconductor material, the second semiconductor material and a second metal material. Notably, the first metal material and the second metal material are the same. In some embodiments, the first metal silicide layer 270 a′ includes TiSi, and the second metal silicide layer 270 b′ includes TiSiGe, but the disclosure is not limited thereto.

Still referring to FIGS. 17A to 17E, a glue layer such as a TiN layer is then formed over the first metal silicide layer 270 a′, the second metal silicide layer 270 b′, sidewalls of an upper portion of the first opening 262 a, and sidewalls of an upper portion of the second opening 262 b. However, in some embodiments, formation of the glue layer can be omitted. Subsequently, a metal layer 264 is formed to fill the first opening 262 a and the second opening 262 b according to operation 120.

Accordingly, a multi-gate semiconductor device 200′ is provided. The multi-gate semiconductor device 200′ includes the multi-gate semiconductor structure 200 a′ and a multi-gate semiconductor structure 200 b′. In some embodiments, the multi-gate semiconductor device 200′ is a CMOS device, the multi-gate semiconductor structure 200 a′ is an n-channel FET, and the multi-gate semiconductor structure 200 b′ is a p-channel FET. As shown in FIGS. 17A to 17E, the multi-gate semiconductor device 200′ includes the plurality of nanowires 232 serving as channel regions for the n-channel multi-gate semiconductor structure 200 a′ and the plurality of nanowires 234 serving as channel regions for the p-channel multi-gate semiconductor structure 200 b′. The multi-gate semiconductor device 200′ further includes the first gate structure 250 a disposed over the plurality of nanowires 232, the second gate structure 250 b disposed over the plurality of nanowires 234, the first source/drain structures 282 a and 284 a disposed at two ends of each nanowire 232, and the second source/drain structures 282 b and 284 b disposed at two ends of each nanowire 234. It should be noted that the first source/drain structures 282 a and 284 a include the first conductor such as the first metal portion 280 a, the first semiconductor layer 220 a disposed around sidewalls and a bottom of the lower portion of the first metal portion 280 a, and the first metal silicide layer 270 a′ disposed between the lower portion of the first metal portion 280 a and the first semiconductor layer 220 a. The second source/drain structures 282 b and 284 b include the plurality of nanowires 230, the second metal silicide layer 270 b′ disposed over the plurality of nanowires 230, and the second semiconductor layer 220 b disposed between the second metal silicide layer 270 b′ and the plurality of nanowires 230. Further, the nanowires 230 and the nanowires 234 are the same nanowires. It is referred that a portion of each nanowire surrounded by the second gate structure 250 b serve as channel regions and are referred to as a first portion 234, while another portion of each nanowire adjacent to and on opposing sides of the channel region form a part of the second sour/drain structures 282 b and 284 b and are referred to as a second portion 230.

As mentioned above, the first metal silicide layer 270 a′ and the second metal silicide layer 270 b′ can include different semiconductor materials but the same metal materials. In some embodiments, the first metal silicide layer 270 a′ includes TiSi while the second metal silicide layer 270 b′ includes TiSiGe. It should be noted that for the n-channel multi-gate semiconductor structure 200 a′, the contact resistance is reduced by forming the low-resistivity first metal portion 280 a. However, by simultaneously forming the first opening 262 a and the second opening 262 b and simultaneously forming the first metal silicide layer 270 a′ and the second metal silicide layer 270 b′, the methods 10 a and 10 b are integrated and simplified while contact resistance of the multi-gate semiconductor device 200′ is reduced.

Embodiments for semiconductor structures and method for manufacturing the same may be provided. The semiconductor structure may include nanowire structures, a gate structure formed around the nanowire structures, a source/drain structure, and a contact plug. The contact plug may extend below the top surface of the nanostructures, so that the contact plug is partially surrounded by the source/drain structure and therefore has a larger contact area with the source/drain structure.

In some embodiments, a semiconductor structure is provided. The semiconductor structure includes a substrate and first nanostructures and second nanostructures formed over the substrate. The semiconductor structure further includes a first source/drain structure formed adjacent to the first nanostructures and a second source/drain structure formed adjacent to the second nanostructures. The semiconductor structure further includes a first contact plug formed over the first source/drain structure and a second contact plug formed over the second source/drain structure. In addition, a bottom portion of the first contact plug is lower than a bottom portion of the first nanostructures, and a bottom portion of the second contact plug is higher than a top portion of the second nanostructures.

In some embodiments, a semiconductor structure is provided. The semiconductor structure includes a substrate and first nanostructures and second nanostructures formed over the substrate. The semiconductor structure further includes a first gate structure surrounding the first nanostructure and a second gate structure surrounding first portions of the second nanostructures and a first source/drain semiconductor layer formed adjacent to the first gate structure. The semiconductor structure further includes a second source/drain semiconductor layer surrounding second portions of the second nanostructures and a first contact plug formed over the first source/drain semiconductor layer. The semiconductor structure further includes a second contact plug formed over the second source/drain semiconductor layer. In addition, the first contact plug extends below a topmost surface of the first nanostructures.

In some embodiments, a method for forming a semiconductor structure is provided. The method includes alternately stacking first semiconductor layers and second semiconductor layers over a substrate and patterning the first semiconductor layers and the second semiconductor layers to form a first fin structure and a second fin structure. The method further includes forming an isolation structure around the first fin structure and the second fin structure and recessing the first fin structure in a first source/drain region to form a first recess. The method further includes forming a first source/drain semiconductor layer over the first recess and removing the first semiconductor layers of the second fin structure in a second source/drain region to form gaps between the second semiconductor layers of the second fin structure in the second source/drain region. The method further includes filling the gaps between second semiconductor layers in the second source/drain region by a second source/drain semiconductor layer and filling the first recess by a conductive material to form a first contact plug over the first source/drain semiconductor layer.

The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure. 

What is claimed is:
 1. A semiconductor structure, comprising: a substrate; first nanostructures and second nanostructures formed over the substrate; a first source/drain structure formed adjacent to the first nanostructures; a second source/drain structure formed adjacent to the second nanostructures; a first contact plug formed over the first source/drain structure; a second contact plug formed over the second source/drain structure, wherein a bottom portion of the first contact plug is lower than a bottom portion of the first nanostructures, and a bottom portion of the second contact plug is higher than a top portion of the second nanostructures.
 2. The semiconductor structure as claimed in claim 1, wherein the first source/drain structure covers sidewalls of the first nanostructures and extends between neighboring first nanostructures.
 3. The semiconductor structure as claimed in claim 1, wherein the second source/drain structure surrounds portions of the second nanostructures.
 4. The semiconductor structure as claimed in claim 1, further comprising: a first gate structure surrounding the first nanostructures; and a second gate structure surrounding the second nanostructures, wherein a bottom surface of the first gate structure is higher than the bottom portion of the first contact plug.
 5. The semiconductor structure as claimed in claim 1, further comprising: a first silicide layer formed over the first source/drain structure, wherein a bottom portion of the first silicide layer is lower than the bottom portion of the first nanostructures.
 6. The semiconductor structure as claimed in claim 5, further comprising: a second silicide layer formed over the second source/drain structure, wherein an interface between the first silicide layer and the first source/drain structure is greater than an interface between the second silicide layer and the second source/drain structure.
 7. The semiconductor structure as claimed in claim 1, wherein a height of the first contact plug is greater than a height of the second contact plug.
 8. A semiconductor structure, comprising: a substrate; first nanostructures and second nanostructures formed over the substrate; a first gate structure surrounding the first nanostructure and a second gate structure surrounding first portions of the second nanostructures; a first source/drain semiconductor layer formed adjacent to the first gate structure; a second source/drain semiconductor layer surrounding second portions of the second nanostructures; a first contact plug formed over the first source/drain semiconductor layer; and a second contact plug formed over the second source/drain semiconductor layer, wherein the first contact plug extends below a topmost surface of the first nanostructures.
 9. The semiconductor structure as claimed in claim 8, wherein a bottommost of the second contact plug is higher than the second nanostructures.
 10. The semiconductor structure as claimed in claim 8, further comprising: first inner spacers separating the first gate structure and the first source/drain semiconductor layer, wherein the first contact plug has a first portion level with the first inner spacers and has a second portion level with the first nanostructures, and a first lateral width of the first portion is greater than a second lateral width of the second portion.
 11. The semiconductor structure as claimed in claim 8, wherein a top surface of the first contact plug is substantially level with a top surface of the second contact plug, and a bottom surface of the first contact plug is lower than a bottom surface of the second contact plug.
 12. The semiconductor structure as claimed in claim 8, further comprising: a first silicide layer formed over the first source/drain semiconductor layer; and a second silicide layer formed over the second source/drain semiconductor layer, wherein the first silicide layer extends lower than the second silicide layer.
 13. The semiconductor structure as claimed in claim 12, further comprising: first inner spacers separating the first gate structure and the first source/drain semiconductor layer, wherein the first silicide layer extends along sidewalls of the first nanostructures and sidewalls of the first inner spacers.
 14. A method for manufacturing a semiconductor structure, comprising: alternately stacking first semiconductor layers and second semiconductor layers over a substrate; patterning the first semiconductor layers and the second semiconductor layers to form a first fin structure and a second fin structure; forming an isolation structure around the first fin structure and the second fin structure; recessing the first fin structure in a first source/drain region to form a first recess; forming a first source/drain semiconductor layer over the first recess; removing the first semiconductor layers of the second fin structure in a second source/drain region to form gaps between the second semiconductor layers of the second fin structure in the second source/drain region; filling the gaps between second semiconductor layers in the second source/drain region by a second source/drain semiconductor layer; and filling the first recess by a conductive material to form a first contact plug over the first source/drain semiconductor layer.
 15. The method for manufacturing the semiconductor structure as claimed in claim 14, further comprising: forming a second contact plug over the second source/drain semiconductor layer, wherein the first contact plug and the second contact plug have different shapes.
 16. The method for manufacturing the semiconductor structure as claimed in claim 14, further comprising: removing the second semiconductor layers of the first fin structure in a first channel region to form first nanostructures; forming a first gate structure surrounding the first nanostructures; removing the first semiconductor layers of the second fin structure in a second channel region to form second nanostructures; and forming a second gate structure surrounding the second nanostructures.
 17. The method for manufacturing the semiconductor structure as claimed in claim 16, further comprising: forming first inner spacers adjacent to the first nanostructures, wherein the first source/drain semiconductor layer covers sidewalls of the first inner spacers.
 18. The method for manufacturing the semiconductor structure as claimed in claim 16, further comprising: forming a first silicide layer over the first source/drain semiconductor layer, wherein the first silicide layer extends below the first nanostructures.
 19. The method for manufacturing the semiconductor structure as claimed in claim 18, further comprising: forming a second silicide layer over the second source/drain semiconductor layer, wherein a bottom of the second silicide layer is higher than a bottom of the first silicide layer.
 20. The method for manufacturing the semiconductor structure as claimed in claim 14, further comprising: forming a dielectric layer over the first source/drain semiconductor layer to fill in the first recess in the first source/drain region before removing the first semiconductor layers of the second fin structure in the second source/drain region; removing the second semiconductor layers of the first fin structure in a channel region to form first nanostructures; forming a first gate structure surrounding the first nanostructures; and removing the dielectric layer in the first recess to expose the first source/drain semiconductor layer before filling the first recess by the conductive material to form the first contact plug. 